Definition: Long oil alkyd based, single component, easy to apply parquet varnish Its brightness, elasticity, impact and scratch resistance are superior features. It protects parquet, tile and other wood surfaces against cleaning agents and chemicals by forming a film layer on the surface where it is applied. It does not change the color of the surface it is applied to. Fiore Glass Polished surfaces can be easily cleaned with soapy or detergent water.
Area of Application: It is used as an ideal protective varnish for parquet, tile and all wood surfaces.
Application Tools: Pistole, Brush, Roller
Method of Application: Care should be given that the surface should be clean, dust-free and dry so that the surfaces to be applied can produce good results. Fioretex Varnish-Free Wood Protection should be applied to new wood surfaces before they can be applied. Parquet defects and gaps are filled with paste to be made with saw-dark mixture when necessary. After drying, excess is cleaned by sanding. It is recommended to be applied 2-3 times to surfaces prepared in this way. 5-6 hours should be waited between coats. After 24 hours, it reaches walking hardness. If the application is to be performed with a brush, the varnish is used without thinning and if it is to be performed with pistole, the varnish is used by thinning at the rate of 10-15%.
Touch drying: 2-3 Hours Dust Drying: 5-6 Hours
Hard drying : 12 hours
The drying time may vary depending on the temperature and air circulation of the application medium and the film thickness coefficient.
Paintable Area: Depending on the type of wood on single coat, an area of 15-17 m2 can be painted with 1 kg.
Storage Type and Duration: 1 year in a cool and dry environment not receiving direct sunlight, sealed packaging (+5°C to +30°C)
(S2) (Keep out of the reach of children.)
(S7) (Store in a closed, cool and ventilated place.)
(R10/11) (Easily flammable)
(R20/21/22) (Harmful by inhalation in contact with skin if swallowed.)
(R36/38) (Irritant to eyes and skin)
Notes: Temperature of the application surfaces should be above +5°C.